ASMET, the Austrian Society for Metallurgy and Materials, invites decision-makers, engineers, developers, industry experts, scientists and students to the fifth Metal Additive Manufacturing Conference with exclusive focus on the processing of metals.
European Powder Metallurgy Association (EPMA) is a non profitable organization promoting metal powder technologies. It represents the powder metallurgy (PM) industry within Europe and Internationally, and develop the future of PM. This is achieved through driving research projects, offer extensive basic and advanced training, numerous seminars and arranging the main yearly PM conference in Europe.
Additive manufacturing (AM) using metal powders has been a focus area with EPMA since 2013. It quickly gained important momentum within EPMA and become the main driver during the yearly conference. It represents the vast majority of technical papers presented. Several internal AM research projects has been conducted by EPMA. On top of that EPMA participates currently in several EU financed projects.
As the Additive Manufacturing (AM) industry moves towards series industrial production, the need for standards covering all aspects of the technology value chain becomes ever more prevalent. While standards and specifications for the various aspects of the AM materials and process chain continue to evolve, many such standards still need to be matured or are under consideration/development within the industry. In particular, materials feedstock, process qualification, testing, evaluation and structural integrity issues continue to be the main focus of ongoing efforts in the standardization community. This presentation will discuss the state of the AM standardization including gaps, challenges, opportunities, and insight based on a recent initiative to establish a global center of excellence to support standard related research and development to be able to close the standardization gaps while contributing to education and workforce development needs as well as qualification programs.
This plenary presentation is focused on the coming manufacturing systems for metal additive manufacturing controlled cyber-physically. Cyber-Physically controlled Smart Additive Manufacturing system (CPSAM) is a smart additive manufacturing system for realizing Industry 4.0/Smart Manufacturing on the shop floor via cyber-physical control scheme. CPSAM is capable of
1) autonomous abnormality resolution via MAPE/BD (Monitoring, Analysis, Planning and Execution based on Big Data analytics and Digital twin),
2) coordination with the shop floor system, and
3) seamless interface with the life cycle aspects, hierarchy levels, and humans.
In other words, CPSAM is capable of intelligent and autonomous functions such as:
• dealing with abnormalities during machine operation,
• coordination with shop floor devices such as robots and material handling system,
• augmented interaction for human-robot collaborative tasks,
• collaboration with the shop floor control system for performance optimization (Key Performance Indicators, KPIs),
• interface with the life cycle aspects, CAx (Computer-Aided Design (CAD), Engineering (CAE), Manufacturing (CAM), and Quality assurance (CAQ), and Manufacturing Resource Planning (MPR II), Product Lifecycle Management (PLM), etc.),
• interface with hierarchy levels, such as Manufacturing Execution System (MES), Enterprise Resource Planning (ERP), Customer Relationship Management (CRM), and Supply Chain Management (SCM).
This plenary presentation will describe the above-mentioned and the possible and ongoing standardization which will set the industrial baseline shortly.
Keywords: Cyber-physical systems, Additive Manufacturing, Artificial intelligence, Sensor systems, Machine learning, Automated reasoning
Complex metallic structures additively manufactured via laser powder bed fusion (L-PBF) is an already established technique in this rapidly growing industry branch. However, the development of alloys for field-specific applications and the quality and functionality of the final parts strongly depends on the micro- and nanostructure morphology, crystallography and chemical composition.
Within this paper correlative microscopy studies performed on 3D-printed parts of Fe- and Ti- alloys are presented [1-4]. Scanning and transmission electron microscopy (SEM and S/TEM) coupled with analytical characterization methods were used for advanced microstructural analysis of the as-built and heat-treated parts. Evolution of the microstructure during the ex-situ heat-treatment was first studied in detail in order to better comprehend the mechanical properties of the printed parts.
Furthermore, in-situ heating measurements at high spatial resolution provided information regarding the evolution of nanometric amorphous/crystalline phases and coarsening/shrinking of grains, diffusion of alloying elements and nucleation and evolution of secondary phases at different temperatures .
This work received financial support by the Austrian Science Fund (FFG): SP2018-003-006 (Microstructure of 3D printed metallic parts) and from the European Union’s Horizon 2020 research and innovation program under grant agreement No 823717 – ESTEEM3.
 Turk, C.; Zunko, H.; Aumayr, C.; Leitner, H.; Kapp, M.: Advances in Maraging Steels for Additive Manufacturing, Berg Huettenmaenn Monatsh., 164 (2019), no. 3, pp 112–116, https://doi.org/10.1007/s00501-019-0835-z
 Albu, M; Mitsche, S.; Nachtnebel, M.; Krisper, R.; Dienstleder, M.; Schröttner, H; Kothleitner, G.: Microstructure Investigations of Powders and Additive Manufactured Parts, Berg Huettenmaenn Monatsh., 165 (2020), no. 3, pp 169–174, https://doi.org/10.1007/s00501-020-00958-3
 Vilardell, A.M.; Yadroitsev, I.; Yadroitsava, I.; Albu, M.; Takata, N.; Kobashi, M.; Krakhmalev, P.; Kouprianoff, D.; Kothleitner, G.; du Plessis, A.: Manufacturing and characterization of in-situ alloyed Ti6Al4V(ELI)-3 at.% Cu by laser powder bed fusion, Add. Manuf. 36 (2020), 101436, https://doi.org/10.1016/j.addma.2020.101436
 Vilardell, A.M.; Takezawa, A.; du Plessis, A.; Takata, N.; Krakhmalev, P.; Albu, M.; Kothleitner, G.; Yadroitsava, I.; Yadroitsev, I.: Mechanical behavior of in-situ alloyed Ti6Al4V(ELI)-3 at.% Cu lattice structures manufactured by laser powder bed fusion and designed for implant applications, J. Mech. Bev. Biomed. Mat. 113 (2021) 104130, https://doi.org/10.1016/j.jmbbm.2020.104130
 Albu, M; Krisper, R.; Lammer, J.; Kothleitner, G.; Fiocchi, J.; Bassani, P.: Microstructure evolution during in-situ heating of AlSi10Mg alloy powders and additive manufactured parts, Add. Manuf. 36 (2020), 101605, https://doi.org/10.1016/j.addma.2020.101605
Additive manufacturing (AM) generates complex multi-scale microstructures in metallic components, differing from conventional microstructures in terms of grain structure, cell substructure, elemental distribution, and residual stress. It is therefore important to analyse AM microstructures across multiple length scales using correlative microscopy techniques to establish comprehensive understanding of the microstructural evolution. This will unlock a greater level of microstructure and property control for future applications of AM.
We investigate 17-4 precipitate hardening stainless steel, a high-strength multi-purpose alloy with applications in the aerospace and petrochemical industries. Samples were fabricated by laser powder bed fusion using a variety of scanning patterns and differing laser powers. We utilise scanning electron microscopy, electron backscattered diffraction, neutron scattering analysis, electron probe microanalysis, and atom probe tomography to characterize the microstructure across different length scales. Results show clear variation in sample texture, residual stress, phase fraction and distribution, and compositional variation as a function of the processing parameters. The main phase of the as-printed microstructure is δ-ferrite with a low volume fraction of austenite, which is mainly observed at melt pool boundaries. The total fraction of austenite increases as the time between adjacent passes of the laser decreases. In the as-printed state, samples are shown to be highly stressed, suggesting heat treatments must be applied before any practical implementation in engineering applications. Higher laser power leads to an increase in ferrite grain size and intensity of <100> texture along the build direction due to the enhanced effect of epitaxial growth.
In recent years, the method of additive manufacturing has become more and more important in the production of magnetic materials due to higher demands for miniaturization and complex- shaped magnet parts. With the method of Laser beam- powder bed fusion (LB-PBF), an in- situ alloying process for the additive manufacturing of the Fe-Cr-Co system has been developed. With this novel method that has been extensively studied in this work, the production of complex alloys with a composition accustomed to each specific case of application can be achieved directly in the printing chamber by the use of elemental powders or simpler commercial alloy powders as base materials.
First, the influence of different printing parameter on the homogeneity of the element distribution in the as- printed samples has been examined by EBSD measurements coupled with EDS. The homogeneity of element distribution in in- situ alloyed samples is not only of crucial importance for the magnetic properties in this material, but also for materials properties of in- situ alloyed materials in general. Obtaining a homogeneous distribution of elements during the in- situ alloying process without the need for a subsequent heat treatment for homogenization can be of economic benefit for the producer. Therefore, the effectiveness of different methods to increase the homogeneity from parameter variation and variation of particle size distribution has been examined.
With this information in mind, the influence of printing conditions and the elemental homogeneity on the microstructure and magnetic properties of the alloy system has been studied by different methods like SEM/ EBSD, TEM, magnetic characterization and dilatometry.
Additive manufacturing is an attractive and now well-accepted technique. Nevertheless, to reach its full potential, the method needs, among other issues, to cope with distortion and residual stress. High, local and quickly moving heat input leads to high temperature gradients that give rise to residual stresses during solidification and cooling. Due to residual stresses, components can crack already during manufacturing, distortions can develop when components are cut off their build plate and fatigue life can be shortened as residual stresses add up to external service stresses.
Numerical simulations based on the finite element method are a well-suited tool to predict residual stresses and resulting distortions. Simulations techniques for additive manufacturing have been derived from simulation techniques previously developed for welding applications. Nevertheless, the very small size and the intensity of the heat source require small elements and small time steps which leads to heavy simulations and long run-times. Drastic simplifications must therefore be made which unfortunately alter the precision of the results. Several methods of different complexity levels are currently available as shown in the following non-exhaustive list:
In this study, these four models are run for the exact same component and process (geometry, material properties, heat source parameters, boundary conditions), see Fig.1, and relevant sensitivity studies are carried out. Distortion results are compared to one another and to actual measurements. As expected, the level of simplification has a strong influence on the reliability of the results.
Figure 1: Actual printed component and simulation model.
A powder atomization plant for the production of high-quality metal powder for Additive Manufacturing (AM) was developed at SMS group. Low cost and simultaneously highest quality powders are key enablers for AM on its way to the next revolution in manufacturing. SMS strives for highest availability, productivity and yield of the powder atomization process through implementation of data-driven analysis of the process.
Due to the activities in the Additive Manufacturing Competence Center at SMS in Mönchengladbach, the powder production process become constantly optimized economically and technically by the aggregated knowledge and data at the pilot plant.
The powder production plant is highly digitalized and generates massive cloud-based production data. Countless sensors in the plant ensure the automated data collection during production. Material flows, pressures, temperatures and positions are recorded in the database. Massive initial data has been collected here over the last two years. SMS is working on the data evaluation and the implementation of Artificial Intelligence. Goals like a self-optimizing process, predictive manufacturing and even predictive maintenance can be realized and guarantees the costumer to be successful.
Metal atomization is a multifaceted process as being represented by different technologies that allow for achieving input material for 3d metal printers, opening the door to new possibilities. The focus area of the 3D LAB company together with their own ATO technology of atomization using ultrasonic system and melting electric arc stand for the key to make the door widely-open while offering a totally innovative approach to powder technology. All this coming hand in hand with a summary of the physics of the droplet formation process, and key features determining the powder median diameter. The possibility to process metal alloys with a melting temperature surpassing 3000ºC enables the user to delve into an even wider range of applications, greatly increasing the efficiency of work directed at the development of new materials. Our intensive development work aimed at the optimization of the laboratory-use atomization process has resulted in successful production of both reactive and non-reactive powders on a smaller, yet still completely self-sufficient scale. The ATO Lab has been designed by industry-oriented researchers, and it is enclosed in a laboratory-sized device which is intended for the use research in development in a range of powder metallurgy areas. Next generation ultrasonic atomizer allows for the production of exceptionally small minimal amounts of spherical powders with a very narrow particle size distribution, as well as obtaining significantly higher yields through continuous operation. With a small footprint form, the device is possible to be used even in restricted spaces. Along with its innovative technology and no requirements for sophisticated infrastructure, it ensures exceptionally low operating costs and quick return on the investment (ROI)
It is now widely accepted that there is an urgent need for a test to determine if a powder can be spread in to thin layers, as it must be for powder bed additive manufacturing. There is not yet any accepted or standardised test for this behaviour. Several techniques have been proposed in the last few years, most based on automated film applicators. A layer can be formed using similar settings to those in a 3D printer and then analysed using optical analysis or by measuring the mass of powder in the layer. The current work outlines recent progress in automated optical analysis of defects in the layer using directional lighting and the effects of dispensing strategy and roughness of the surface on which the powder is spread. A discrete element model has also been made and compared to experimental findings to benchmark the capability of the technique to replicate reality.
Laser powder bed fusion (LPBF) facilitates near-net-shape fabrication of geometrically complex tools. This leads to significantly reduced post-processing effort compared to conventional manufacturing, for example in the case of hobbing cutters. However, due to the high carbon equivalent of high-speed steels, cracking of the brittle carbon martensite is very likely during LPBF. In contrast, carbon-free maraging steels promise enhanced processability due to the formation of a soft martensite. Hardening of the latter is guaranteed by the precipitation of intermetallic phases. A novel maraging steel for cutting applications (Fe25Co15Mo (weight%)) has been developed in recent years. This alloy might therefore be a candidate for LPBF.
In the present work, the LPBF processability of this novel cutting alloy was investigated. Despite its low carbon content, severe cracking has been observed. The crack surface analysis revealed transcrystalline cleavage fracture. It is assumed, that silicon oxide inclusions on the crack surface are responsible for this brittle failure. Additionally, epitaxially elongated coarse grains were found, which may also contribute to cracking. An influence of brittle ordered FeCo domains, that are potentially formed during cooling in the LPBF process, could not be confirmed. Based on the obtained findings, solution approaches for the fabrication of crack-free parts are presented.
Additively manufactured (AM) samples exhibit a pronounced texture formation along the build direction (i.e. along z-axis) that predefines an anisotropic mechanical behavior of the final bulk materials. Consequently, different mechanical properties can be measured in tensile tests along and perpendicular to the build direction, depending on the initial orientation of the sample in the powder bed. In this study, we investigated the influence of three different hatching strategies on the texture formation of stainless steel 316L. Therefore, six rod-like samples (Ø 5mm, 40 mm height) were synthesized on an EOS M290 machine using two different parameter sets. The samples were scanned in transmission geometry at the high-energy material science (HEMS) beamline P07B at the storage ring PETRAIII at DESY in Hamburg using an energy of 87.1 keV. The three applied scanning strategies led to the formation of (i) a <001> fiber texture, (ii) a biaxial texture and (iii) a mixture of <100> and <110> fiber textures. Moreover, micro-tensile samples (with a diameter of ~500 µm) were fabricated and tested to assess the mechanical properties. Observed differences could be correlated with the different textures. The results indicate that the mechanical properties of AM bulk metals that can be effectively tailored by adjusting the crystallographic texture within the AM components.
Due to the raster heat inputs, steep temperature gradients and rapid cooling, the selective laser melting (SLM) process generally induces high residual stresses heterogeneity across the fabricated parts. In the case of gears, such variations on the teeth flank may have a negative effect on the fatigue behavior. This study analyzes the influence of residual stresses heterogeneity induced by SLM on the contact fatigue behavior of carburizing steel 20MnCr5 samples reproducing gear applications. Residual stress maps and depth profiles obtained by X-ray diffraction along the dimensions of rod-shaped samples are correlated to ball-rod contact fatigue results. The fatigue scatter is then discussed in view of the residual stress heterogeneity.
This study aims to investigate the influence of different process gases on the processing of a Zr-blended aluminum 7075 alloy by laser-based powder bed fusion. Two common gases for this process, argon and nitrogen, are compared. The objective is to study the effect of the gases on crack formation in the bulk material with respect to the possible formation of nitrides. In order to assess this phenomenon, bars at different heights will be printed with an in-situ change of the process gas in steps from pure argon to pure nitrogen. During the post-process analyses, special focus will be placed on investigating the crack formation. The preliminary results on specimens from initial build jobs showed differences in the cracking behavior with a varying amount of nitrogen in the process gas. A higher amount of cracking was found in the specimens produced with pure nitrogen compared to the specimens fabricated under argon atmosphere. This may be due to less Zr dissolved into the aluminum matrix under nitrogen processing conditions. The higher amount of cracks might therefore be attributed to the creation of fewer Al3Zr-precipitates that are needed for grain refinement and crack mitigation in this aluminum 7075 alloy.
The provision of the metal raw material (due to a low product yield) and inert gas consumption are the main energy consumers in powder production for additive processes. In standard gas atomization processes, any effort to produce finer powder (to increase product yield) is achieved by increasing inert gas consumption.
In order to decrease the carbon footprint of additively manufactured parts, a new powder production process was established at Metalpine GmbH. With the inhouse developed combination of melting system, gas atomization nozzle and closed gas circuit, high product yields are achieved at a strong decrease of gas consumption. The resulting powders are spherical, satellite-free and pore-free.
First evaluations of the printed parts show that the mechanical properties of the printed parts are compareable to the ones printed with powders from long-time established powder production processes.
A continuous growth for high quality metal powders in Additive Manufacturing applications forced INTECO to develop a novel vacuum inert gas atomization system, as standard atomization equipment has not seen major developments or improvements to fulfill the demanding tasks from the industry. The new system is characterized by special features which are supposed to overcome disadvantages of common atomization systems, like low yield or limited reproducibility. A peculiar focus was put on the automation of all process steps, including the casting and atomization procedure. This is essential to eliminate undesired influences from operators which would end in a significant volatility of the powder´s properties. Additionally the plant is designed to achieve a quick and precise cleaning of all parts when changing the produced grades. The high pressure gas nozzle was developed to not only grant a high efficiency but also to manufacture powder particles with low amounts of satellites. Low tap-to-tap times are achieved by optimized and synchronized process steps like evacuation, melting, atomization, and powder handling. Latter is supported by a unique powder cooling for a quick availability of the produced powder for subsequent operations. With the help of an integrated production management tool called IMAS the complete production is logged and documented.
Results of the commissioning of two plants including production experience is presented. The practical knowledge lead to further aspects of possible improvements. An outlook is given towards ongoing and further developments.
In Laser Powder Bed Fusion (LPBF), a significant amount of metallic powder is not melted by the laser beam. Costs and material yield strongly depend on the ability to reuse metal powder efficiently. However, some of the unfused powder is exposed to high temperatures during the manufacturing process in an imperfectly controlled atmosphere. Therefore, there is a need to study and understand powder degradation during the process and its direct effects on the printed parts. One batch of gas-atomized 316L stainless steel powder was used, recovered, sieved and reused to produce 12 successive LPBF prints without adding any virgin powder. Both recycled powders and elaborated parts were characterized throughout each iteration. Particles analysis was carried out using laser granulometry, scanning electron microscopy, flowmeter funnels, inert gas fusion, and X-ray diffraction. Solidified specimens features were investigated by means of optical microscopy, scanning electron microscopy, electron backscattered diffraction, microhardness and uniaxial tensile testing. Powders morphology, rheology, microstructure and oxygen content display slight changes with recycling, along with parts density and mechanical properties. The effects of processing conditions, especially the chamber oxygen content were also studied, and strongly influence the kinetics of degradation.
Within this contribution, the transfer of knowledge from conventional fusion and deposition welding using electric arc processes to advanced direct energy deposition (DED) of multi-material structures in additive manufacturing will be presented. Gas metal arc and plasma welding have been used for decades to produce either joints or metallic deposits with desired properties. Also creating certain shapes by depositing weld metal in a layer-wise manner is known for approximately 100 years. With the rise of additive manufacturing, conventional arc welding processes have been extensively used to “print” 3-dimensional parts. The possibility of additively manufacturing multi-material parts or transition parts is of particular interest, as this has the potential to create load-efficient structures or even new alloys within the AM process.
Within this presentation, Wire Arc Additive Manufacturing (WAAM) and 3D Plasma Metal Deposition (3DPMD) for the manufacturing of multi-material and transition parts will be discussed. The experience with various alloys from carbon steels, high-alloyed steels and titanium- and nickel-based alloys will be presented.
3D-printing of implants, tools or prostheses in a clinical setting is a highly challenging field in additive
manufacturing. It is crucial to guarantee patients as well as attending physicians at any time the highest
possible quality of material as well as printing process and this quality of course has to be reproducible
and on the highest possible level.
These requirements in the highly sensitive medical setting are highly challenging to fulfil and a broad
range of preclinical investigations have to be done, before 3D-printed can be included to the clinical
The COMET K-Project CAMed funded by two Austrian public institutions aims to bring the highly
promising technology of 3D-printing into a clinical setting to optimize treatment options by
manufacturing patient-specific implants. Companies supporting this project in the area of polymers
are Apium Additive Technologies, ARBURG and HAGE3D, who provide the innovative printing
technologies such as Fused Filament Fabrication for low and high temperature polymers or ARBURG
In the first two project years of CAMed, optimal printing parameters for various promising materials
were developed together with the scientific project partners. Printed samples were analysed on their
mechanical characteristics by bending and charpy tests as well as on their clinical sterilizability and
biocompatibility. Together with segmentation and simulation of patient data and a close cooperation
with scientific partners for process development and optimization, the chance of integrating 3Dprinting
into the clinic within the next two years is getting closer and closer.
Different aspects of quality assessments for Additive Manufacturing (AM) parts are founded on complicated phenomena governed by intrinsic multi-physical and multi-phase interactions. To investigate the dynamic and fatigue performances of AM parts, variety of techniques including new hybrid physical-data driven scheme have been investigated. Hybrid modelling is one of the new trends in analyses and design optimization of AM parts where data modelling techniques have increasingly been combined with physical and analytical modelling for dynamic and fatigue assessments. An effective use of appropriate modelling schemes for fatigue analyses of AM parts and their agility of dealing with sophisticated effects of the manufacturing processes (e.g., defects, pores…) on service-life of products would briefly be reviewed herein. With the introduction of hybrid physical-data driven modelling techniques for the new AM process technologies and digitization drive, the need for integration of smart data-driven and physical-based models has willingly raised in the current research work. Different hybrid and data-driven schemes which include data mining, data handling, data processing and data modelling have rigorously been employed by researchers and engineers for dynamic and fatigue life simulation of AM parts at industrial scale. Furthermore, attempts have been made to setup full integrated data-bases where the available measured\mined\simulated data which are based on material characteristics and process conditions can semantically be gathered within single data depository. In the research work herein, some aspects of hybrid fatigue life assessment scheme for AM parts have been reviewed and analytical and computational benefits are scrutinized. Additionally, the employment of an efficient artificial Intelligent (AI) and Machine Learning (ML) schemes for industrial AM parts are tersely presented.
The rise of additive manufacturing has enabled new degrees of freedom in terms of design and functionality. In this context, this contribution addresses the design and characterization of structural unit cells that are intended as building blocks of highly porous lattice structures with tailored properties. While typical lattice structures are often composed of gyroid or diamond lattices, this study presents stackable unit cells of different sizes created by a generative design approach to meet boundary conditions such as printability and homogeneous stress distributions under a given mechanical load.
Suitable laser powder bed fusion (LPBF) parameters were determined for AlSi10Mg to ensure high resolution and process reproducibility for all considered unit cells. Stacks of unit cells were integrated into tensile and pressure test specimens for which the mechanical performance of the cells was evaluated. Experimentally measured material properties, applied process parameters, and mechanical test results were employed for calibration and validation of finite element (FE) simulations of both the LPBF process as well as the subsequent mechanical characterization.
The obtained data therefore provides the basis to combine the different unit cells into tailored lattice structures and to numerically investigate the local variation of properties in the resulting structures.
Plasma Metal Deposition (PMD) is a Direct Energy Deposition (DED) method which allows to fabricate large and heavy parts by using wire or powder as feedstock which are fed into a plasma arc. PMD® allows the building of structures using deposition rates in the kilogram range. Besides the manufacturing of structural parts, the PMD process can be used for the fabrication of integrated cooling structures. Additionally, the combination of wire and powder feedstock allows to integrate hard facing surface directly on the 3D fabricated part. Tools or moulds used for carbon fiber composite manufacturing with integrated cooling channels allow to increase the processing speed in the manufacturing due to reduced cycle times.
In the Horizon 2020 project MULTI-FUN, the manufacturing of fully integrated multi-functionalities of metal parts is in the main focus. These functionalities include enhanced active/passive heat management embedded fibre-optical sensing as well as integrated electrical conductivity.
Several additive layer manufacturing technologies are under development to generate both the internal functional layers (lines/layers/volumes) as well as the final outer geometry of structural parts or manufacturing tools.
In this paper, the sequential application of several direct energy deposition technologies and different material, respectively, is presented, aiming at a multi-material setup offering electrical conductivity. Aluminium is used as a substrate as well as for the filler wires used for the last step of covering the multi-material design by wire+arc AM.
Between substrate and WAAM layer, a stack of layers providing isolation (by aluminium oxide) and electrical conductivity (by copper) is deposited.
The investigations contain variations in layer design, the presented results include electrical and mechanical properties in as-built as well as mechanically loaded conditions as well as microstructures of materials and their interfaces.
The industrial application of embedded electrical conductors in several demonstrators developed in project MULTI-FUN will be addressed.
In laser powder bed fusion processes, spreading as dense and fully covered powder layers as possible is of crucial importance for good processability of powders. Poorly covered layers or layers with unappropriated features in it such as for instance elongated, powderless craters in the direction of spreading might result in insufficient quality of the printed parts. The reason for this could be either poor powder quality or a poorly adjusted build job. To investigate the surface coverage of a single spread layer, a new method was developed using the Spreading Tester. With this, two powder grades differing mostly in their shape were used to investigate the impact of powder shape on the surface coverage.
Bioresorbable materials for use in medical implants are attracting interest in current research projects. Recent studies show promising results for Zinc-Magnesium (ZnMgx) alloys as biodegradable materials due to the combination of degradation rate and high strength resulting from grain refinement due to magnesium addition. By using Additive Manufacturing (AM), complex scaffold-like structures and patient-specific implants can be realized. This work aims to clarify the effect of AM process parameters and magnesium content of binary ZnMgx alloys on the relative density and resulting mechanical properties. Furthermore, process monitoring and non-destructive testing will be explored for quality assurance.
For the experiments atomized pure Zn and pre-alloyed ZnMgx powder is used. The test specimens are manufactured on a modified Laser Powder Bed Fusion (LPBF) laboratory system with tailored shielding gas circulation. For each alloy, cuboid test specimens with different energy inputs are manufactured and evaluated regarding relative density. Next, one set of parameters is chosen to manufacture cylinders and lattice-structures from those alloys in order to determine the mechanical properties. In addition, Optical Tomography will be used to detect irregularities and µCT data will be matched to ensure a reproducible manufacturing of samples. This gathered information will be used to manufacture a bioresorbable implant as a medical demonstrator using LPBF.
Most alloys used in laser powder bed fusion (LPBF) are conventional materials, which were designed for specific conventional processes and their constraints. These alloys are not capable to adapt to the special conditions in LPBF process e.g. the rapid solidification and cyclic heat treatments. Therefore, thermodynamic simulations are used to design new alloys for additive manufacturing (AM).
However, testing digitally developed alloys under real LPBF conditions generates great effort in powder manufacturing. To minimize these costs and reduce time for material development, Fraunhofer ILT has developed the miniaturized and modular process chamber “Petit”, which can be integrated into existing LPBF-systems. While the module uses the optical- and laser system of the existing LPBF machine, it allows the utilization of significantly reduced amounts of powder material (approx. 300 ml) to manufacture material samples from elemental powder blends. Furthermore, the transferability of the results to large processes is given.
Stainless steel (SS) of type 316L is one of the go-to materials for metal additive manufacturing (AM), due to its good weldability. As-printed 316L SS made by AM has unconventionally good mechanical properties exhibiting both high strength and high ductility. However, the corrosion resistance is inadequate, and not on par with conventional 316L. Our research team has demonstrated proof of concept for the lab-scale manufacturing of modified 316L with excellent corrosion resistance combined with superior mechanical properties as compared to “conventional” AM. The method entails modification of the feedstock powder, while the MAM method remains unchanged. The microstructure of the modified 316L is comparable to that of 316L manufactured by L-PBF. Elongated austenite grains with the mechanically beneficial internal cellular substructure were obtained. The powder modification resulted in a Vickers hardness increase of about 40 HV0.1 in the as-built condition. The modification also improved the corrosion resistance, as measured by weight loss after immersion in 5.6% FeCl3 solution for 10 days.
The method has also proven useful for strengthening of duplex stainless steels, and is also expected to be applicable for achieving strength and corrosion resistance in ferritic stainless steels, and for enhancing the AM processability of martensitic stainless steels. The present contribution will also showcase different aspects and applications of the technology.
During the last 20 years, the terms referring to “Additive Manufacturing” (AM) have evolved significantly. In the early days, reference was made to a process called “rapid prototyping” and “rapid manufacturing” was the consecrated term. This terminology remained even beyond the time in which the community started realising that, in fact, it is not necessarily a rapid process. While fashionable names such as FFF, standing for Free Form Fabrication, or Direct Manufacturing came and disappeared, today mainly two terms are employed: “3D printing” when speaking to a public audience and “Additive Manufacturing” when addressing a technical one. AM technologies represent a world of opportunities for innovation and change the way we think about manufacturing, in particular for highly demanding applications like those encountered in Space Industry. However, understanding what is required to use AM for critical space applications remains challenging.
ESA, the European Space Agency, took a leading role in the development of AM for space starting from the early 2010s. The developments funded by ESA began with mildly loaded brackets and now cover an always-expanding panel of space applications. It quickly became apparent that alongside every successful development new challenges arise that need to be resolved. This presentation will bring insight into some of the completed developments of the past 10+ years which shaped current and future development paths of AM for Space. The focus is ensuring the availability of technologies that will allow designing, manufacturing and testing the next generations of European spacecraft. The presentation will also address the different markets and their associated challenges.
Geometric accuracy of parts manufactured by Laser Powder Bed Fusion (LPBF) is deteriorated by powder particles sintered to the part surface as well as excessive melting due to overheating by limited heat flow at sharp contour corners. While the sintered powder particles increase the surface roughness, overheating leads to deviations of the as-built part geometry from the CAD geometry. Use of pulsed wave Laser Powder Bed Fusion (pw-LPBF) has shown an increase in detail resolution as well as an improvement of the part accuracy in the field of micro Powder Bed Fusion (µ-PBF) due to improved melt pool controlling by discrete solidification of adjacent melt pools generated by the laser pulses. However, process efficiency (e.g. build up rate) of pw-LPBF is in general lower compared to continuous wave LPBF (cw-LPBF). Hence, to transfer the results to large-scale parts, an adaptive processing strategy is developed for alloy Inconel 718. Pw and cw laser emission are combined, while pw irradiation is used for contour exposure and cw irradiation for volume exposure, respectively. In this study, process parameters are developed for different part geometries (e.g. sharp contours). Geometric deviations and surface quality of the parts are evaluated using light optical microscopy, Scanning Electron Microscopy and optical surface measurement, respectively. It can be shown that both geometric accuracy and surface roughness is improved by pw contour exposure compared to state of the art cw exposure while sufficient process efficiency is ensured by cw volume exposure.
Additive manufacturing of heat treatable low alloy steels by
Laser beam powder bed fusion (LB-PBF) offers a number of difficulties,
which is the reason why their use in commercial AM is rather limited
today. In the present study, processing of several AISI 4xxx type steels
(Cr-Mn-Mo alloyed) has been studied, and the processing windows have
been defined for 2 different machines, with particular focus on the
laser power. Furthermore, typical defects occurring when processing is
done outside the optimal windows were investigated by metallographic
Carbon-containing ferrous alloys with >0.2 wt.% carbon are considered difficult to weld materials and are thus expected to have poor processability when using Laser Powder Bed Fusion (L-PBF). This is connected to the high cooling rates of L-PBF that result in the formation of martensite and internal residual stresses that create a significant risk of cold cracking within the material. However, the characteristics of martensite formation, its substructure and its properties in L-PBF produced ferrous alloys is a subject that remains poorly understood. Presented work summarizes the effect of carbon on the formation and properties of martensite over a range of model Fe-C alloys as well as low-alloy steels, with a specific focus on martensite properties and its effect on L-PBF processability. This was done using a combination of hardness measurements, optical and scanning electron microscopy, transmission electron microscopy and atom probe tomography, that helped analyze the substructure, carbon distribution and precipitation within L-PBF produced martensite. Results indicate that ferrous alloys with up to 0.75 wt.% carbon can be produced defect-free by tailoring the laser scan strategy and build plate preheating to enhance the intrinsic heat treatment that takes place during processing.
Laser Metal Deposition (LMD) is an established repair process for components such as thin-walled turbine blades. Repair of thin-walled structures encounters several challenges due to the limited heat transfer. If the narrow process window is not met, mechanical properties and geometric accuracy deteriorate. Because of the rising temperature during the LMD process, its parameters usually need to be adjusted with increasing build height. Currently, the development of repair processes for thin-walled structures is usually based on iteratively adjusting the process parameters. For a predictive process development, the fundamental influence of LMD process parameters on part deviation and the resulting mechanical properties must be understood. In this paper, the influence of build strategy and process parameters such as laser power and feed rate on geometric accuracy and resulting residual stresses is investigated. To approximate the heat transfer within thin-walled structures, material is deposited onto the edges of IN718 sheets. In situ thermography is used to study the temperature curve. Furthermore, geometric accuracy and residual stresses are measured post mortem.
The inherent inhomogeneity and cyclic thermal loading in metal additive manufacturing (AM) significantly change the microstructural evolution and various types of solid/solid interfaces compared to traditional routes. However, the same AM characteristics will enable targeted microstructure and property control if the current fundamental understanding of the underlying phenomena can be extended.
In our own recent research as part of the so-called AUSMURI project, we have made exciting discoveries which enable tuning of interface characteristics for property control directly during 3D printing, without complex thermo-mechanical treatments in large metallurgical plants. This presentation will showcase selected recent results on the role of interfaces during AM of Ti-6Al-4V and various stainless steels for defence and other applications.
Analysis of various interfaces formed during electron-powder-bed-fusion of Ti-6Al-4V clarifies the competition between different modes of -variant selection in determining the final microstructure. Understanding of the complexity of the -laths in 3D using plasma focused-ion-beam serial sectioning and electron back-scatter diffraction provides new insights into the fundamental phenomena behind the microstructural evolution in this alloy [1-4].
Further current results are concerned with tuning the crystallographic and chemical grain boundary microstructure and related mechanical and corrosion properties in austenitic, duplex and precipitation hardening stainless steels. This is achieved either directly via variations of the laser-powder-bed-fusion scanning strategy and/or short post-processing heat treatments [5,6].
 P.L. Stephenson, N. Haghdadi, R. DeMott, X. Liao, S.P. Ringer, S. Primig, Additive Manufacturing 36 (2020) 101581.
 N. Haghdadi, R. DeMott, P.L. Stephenson, X. Liao, S.P. Ringer, S. Primig, Materials & Design 196 (2020) 109177. OPEN ACCESS
 R. DeMott, N. Haghdadi, X.Z. Liao, S.P. Ringer, S. Primig, Journal of Materials Science 56 (2021) 14763-14782.
 R. DeMott, N. Haghdadi, Z. Gandomkar, X.Z. Liao, S.P. Ringer, S. Primig, Materialia 20 (2021) 101201. OPEN ACCESS
 N. Haghdadi, M. Laleh, M. Moyle, S. Primig, Journal of Materials Science 56 (2021) 64-107. OPEN ACCESS
 M. Laleh, A.E. Hughes, M.Y. Tan, G.S. Rohrer, S. Primig, N. Haghdadi, Scripta Materialia 192 (2021) 115-119.
Lithographic additive manufacturing (AM) technologies are based on the concept of photopolymerization and are known for their process inherent high precision and good surface quality compared to other AM techniques. In this work, metallic suspensions comprising a photoreactive binder and 316L powder (50vol%) were used as starting material. After printing, the obtained green parts undergo a subsequent thermal treatment similar to what is done in metal injection molding (MIM). After this debinding stage, the structure can be sintered to a relative density of 98.5%. By this approach highly complex parts made of 316L could be manufactured showing a good geometrical accuracy and very low surface roughness; the mechanical properties of the AM structure are comparable to conventionally manufactured 316L (tensile strength > 500MPa). Since the final part is developed by a classical sintering process, the same basic microstructure as in MIM is realized.
Additive manufacturing (AM) has gained traction in orthopedics, so why isn’t it a plug-and-play technology yet? While AM has existed for years, mass implementation takes longer than most expect because AM requires a different approach to design and comprehensive knowledge of the entire process. This presentation will review ways that AM can add value and save when design and process are properly planned and executed.
AM requires important design rules. The technology adds or melts layers. Therefore, there is a limit on the angle for overhanging surfaces. Engineers must think about the build orientation. In the event that large overhanging surfaces can’t be prevented, support material (SM) is needed. This material will support the layers on top of this SM and also function as a heat sink. Residual stresses occur due to rapid heating and cooling. SM can transfer this heat to the build platform and make sure that the part doesn’t deform or crack. These design rules can differ between the SLM and EBM process. Furthermore, the full AM process must be taken into account. Parts made by AM undergo more process steps than those that are traditionally manufactured. SM has to be removed, parts have to be clamped for milling and if required, marking is needed. Designing for the right AM process and the whole process chain has a high-added value.
Consistent part quality needs to be confirmed through validation of the whole AM process. Speeding up the implementation of AM requires more than just attention to manufacturing. The whole process chain has to be taken into account. While this way of thinking takes more time up front in the commercialization process, it allows for proper AM execution and will save time and money in the end.
During the last ten years, additive manufacturing by using power bed fusion technology has become a very reliable technology to produce complex metallic parts. Layer by layer manufacturing allows the integration of a fiber bragg grating inside the parts during the fabrication. The latter opens a lot of possibilities for structural health monitoring. It has a critical impact for the monitoring of the nuclear structure and nuclear waste management, and allows to assess the usability of the parts without taking any risk of outside aggression on the sensor such as corrosion or break during the transport. The methods used during our analysis were the following: i) a parametric study of the laser powder bed fusion processing conditions for 316L stainless steel parts; ii) a study for the adaption of the optical fiber (thermal resistance, impact of the laser, diameter); iii) the optimisation of the bonding between the optical fiber and the metallic component. Fibers have been successfully embedded without coating inside the parts, which demonstrates the feasibility to insert components into the additive manufacturing process. The structural and the mechanical behaviours of the parts remain the same after the insertion of the fiber.. As a conclusion our results show the possibility to embedded a fiber without coating and it could become a game changer in structural health monitoring.
The process-inherent advantages of Laser Powder Bed Fusion (L-PBF) have been exploited for many different applications nowadays, including the production of highly stressed inserts for the Al die-casting industry. However, similar to conventional production routes, performance and lifetime of AM-produced tools are still significantly determined by the specific material properties. Here, high-performance tool steels as the BÖHLER W360 AMPO places highest demands with tight specifications on the L-PBF process in order to exploit its full potential. Against this background, extensive developments have been carried out in order to fully understand the specific process and material interactions for the BÖHLER W360 AMPO, processed on advanced L-PBF Systems. Therefore, this study provides an overview about extensive characterizations of the microstructure, process-induced defects and the obtained mechanical properties. Furthermore, it is demonstrated why this challenging production route is still worthwhile from a holistic point of view and which possible advantages can be derived for further applications.
Inconel 625 is a solid-solution strengthened alloy of great interest for the aerospace and oil and gas industries, due to its good mechanical and corrosion properties, besides microstructure stability up to 540 °C, providing a great potential for the additive manufacturing segment. In this study, Sandvik Osprey Inconel 625 powder, atomized via vacuum induction melting inert gas atomization (VIGA), was printed via laser powder bed fusion process (L-PBF) and specimens were evaluated in terms of microstructure and mechanical performances. The VIGA process allows the production of powders with high circularity and limited satelliting, which positively contributed to achieve highly dense printed specimens. Solution annealing was done at different conditions in order to evaluate the best performances: 1048 °C followed by air cooling or water quenching, and a lower annealing temperature, 1000 °C followed by air cooling aimed to minimize grain growth. Microstructural analysis was carried out for all variants, including as-built condition in order to observe potential cellular structure, segregations and the microstructure evolution for the different annealing routes. Mechanical testing, including tensile, impact and hardness measurements were performed at room temperature for all the considered variants. High temperature tensile testing at 540 °C was done after annealing at 1048 °C and air cooling to evaluate the potential for the Sandvik Osprey VIGA Inconel 625 powder to be used at these temperatures.
Im Rahmen des Vortrages werden neu entwickelte Hochleistungswerkstoffe der AM Metals GmbH und Ihre Anwendungsfelder im Automobil vorgestellt. Dabei werden die spezifischen Beanspruchungen und Anforderungen anhand beispielhafter 3D Druck Applikationen veranschaulicht. Durch gezielte Legierungs- und Prozessentwicklung wurden Aluminiumwerkstoffe entwickelt, die sowohl das Festigkeitsniveau konventioneller Knetlegierungen (EN AW 7075) als auch vergleichbar gute Korrosionseigenschaften von Schmiedewerkstoffen (EN AW 6082), erreichen. Anhand von Mikrostrukturanalysen werden die Eigenschaften und Herausforderungen der Prozessentwicklung veranschaulicht. Fatigue und Kriecheigenmschaften werden im Vergleich zum Stand der Technik diskutiert.
Die fertiglegierten Pulver sind frei von keramischen Bestandteilen und können deshalb einfach im Umlauf wieder genutzt werden. In Verbindung mit der einfachen Rezyklierbarkeit leisten die neuen Werkstoffe einen Beitrag für ein positives LCA des Gesamtsystems.
Die AM-Metals GmbH ist ein Entwicklungspartner zur Applikations- und Prozessentwicklung im metallischen 3D Druck. Ausgehend von der konstruktiven Bauteiloptimierung, über die fertigungstechnische Realisierung auf Systemen des Anlagenherstellers EOS (Serie M), bis hin zur Qualitätssicherung, Wärmebehandlung, Oberflächenfinish und CNC Bearbeitung, können alle für den additiven Prozess notwendigen Fertigungsschritte hausintern abgedeckt werden.
Die AM Metals GmbH gehört zur Dr. H.J. Langer Gruppe.
In contrast to the single-stage process, high deformation degrees can be achieved using multi-stage deep drawing strategies. However, the first forming step already leads to significant changes in the overall sheet metal forming behavior. Temperature changes are caused by friction and plastic deformation in an inhomogeneous manner, which in turn affect the whole subsequent drawing steps and the final part itself.
As worst case, deep drawing components in question may already fail during the first drawing step due to excessive formation of deformation-induced martensite or delayed cracking, which might happen to the final part even hours or days after production.
In this study the influence of the tool temperatures are investigated to reduce the residual stresses and the martensite content. As a result, the forming forces and sheet metal thinning can significantly reduced.
For this purpose, a special 3D printed tool is tested, which is manufactured by selective laser melting (SLM) and offers the possibility to temper the blank holder, the die and the punch.
The results show that an optimized tool temperature strategy reduces the forming forces, residual stresses, martensite content and sheet metal thinning for the metastable austenitic steel used.
The paper presents a part of an integrated experimental chain to manufacture new advanced biodegradable Mg-based implants from powder raw materials by Selective Laser Melting (SLM). The Mechanical Alloying (MA), as a complex solid-state synthesis procedure, was used for obtaining Mg powder alloys with different compositions in the system Mg-xZn-yZr-zCa: Mg-4Zn-0.8Ca-0.5Zr, Mg-6Zn-0.8Ca-0.5Zr and, Mg-10Zn-0.8Ca-0.5Zr. The targeted scientific objectives were to achieve the quality of the powders which is a determinant factor during additive manufacturing – SLM 3D printing; the quality of the powders affects the processing conditions such as flowability, packing of the powders, nature of heat transfer, layer thickness and surface roughness. Many process variables need to be controlled in order to achieve the desired performance-related properties of powders, suitable for SLM. The morphology, grain size distribution and contamination of the milled powders strongly depend on the process variables in mechanical alloying such as milling time, process control-agent, ball to powder weight ratio, the milling atmosphere, etc. Mechanical alloying experiments were carried out for different milling times and speeds using stainless steel balls and a process control agent (i.e. 3% n-heptane solution) to avoid excessive cold welding between powder particles and to inhibit agglomeration. A complex chemical and structural characterization was performed on the obtained powder alloys.
As Additive Manufacturing (AM) technologies mature, the lack of tailored alloys becomes more and more of an obstacle for a widespread application for AM. Alloy development has historically been a costly process taking decades or centuries. In the case of AM, however, new improved alloys have to be developed much faster, calling for time- and resource-efficient alloy development methods. These methods have to fulfill two essential criteria: firstly, in situ alloy mixing must take place locally. Secondly, the cooling rates must be controllable in a wide range in order to match different AM processes ensuring matching microstructures and mechanical properties.
The newly developed Extreme High Speed Laser Material Deposition (EHLA) process meets these two criteria. However, the correlations between its numerous process parameters, resulting cooling rate and microstructure are not yet understood. In this paper, the influence of parameters such as laser power, process speed and powder mass flow on resulting cooling rate and microstructure of 316L is studied using metallographic methods and Scanning Electron Microscopy (SEM). Process parameters with a significant influence on cooling rate and microstructure will be determined, taking one of the first steps for alloy development guidelines for AM.
EOS and Linde combined their respective expertise to jointly undertake research in the field of additive manufacturing and material-gas interaction. The aim of this study was to improve AISi10Mg properties according to customer needs. The influence caused by different impurities of the process gas on the generated material quality as well as the influence on the process itself were analyzed.
In this study the influence of residual oxygen and a special shielding gas mixture during the DMLS® process in relation to the material properties of AlSi10Mg were investigated. With higher oxygen levels the variance of the material properties can increase, as can powder quality and life-cycle due to oxidation.
Nevertheless, in terms of porosity only a minor change in the maximum defect size can be observed when the oxygen level is decreased. Results confirm a quite stable process behavior of AlSi10Mg when using EOS AlSi10Mg powder material, optimized process parameters and the EOS M290.
First analyses of the recorded OT-Monitoring data show a visible influence when using the argon/helium mixture. Special gases like these have a slightly higher price, but if the scrap rate can be reduced, a business case for this gas mixture could be possible.
In addition to the material and process results, there were interesting learnings in terms of the hardware used. To avoid a variation in the oxygen level during the DMLS® process, it is necessary to have a closed loop control to maintain the residual oxygen content within the process gas. The positioning of the oxygen sensors is important and thanks to this study, the optimal location close to the platform was ascertained.
EOS and Linde will continue to work closely together to develop a controllable shielding gas atmosphere for both existing and upcoming DMLS® systems like the EOS M290.
The use of bioresorbable materials for orthopaedic devices allows the sparing of the second (removal) surgery and could enhance bone regeneration mechanisms. One promising candidate from the biodegradable metals is Magnesium (Mg) as it comprises several advantages: degradability within the human body, high biocompatibility as Mg is part of our daily nutrition system and mechanical properties similar to those of human cortical bone, thus avoiding stress shielding. Bone ingrowth can be enhanced by complex lattice-like structures, only feasible by additive manufacturing. Magnesium-Yttrium-Rare Earth (Mg-Y-RE) alloy, originating from aviation industry, showed good biocompatibility and therefore was utilised in this study.
The influences of Laser Powder Bed Fusion process parameters, powder storage conditions and tensile specimen design on the mechanical behaviour were investigated. Density measurements by microscopy of cross sections were carried out for several parameter sets to identify suitable process parameters. Three sets of suitable process parameters were further investigated for their mechanical properties by means of standard tensile specimens. Additionally, we introduced a novel tensile scaffold specimen design, representing a geometry closer to a real case application and allowing to apply the process parameters for scaffold manufacturing. Finally, we compared our results to a corresponding FE-Analysis of uniaxial tensile test.
Zr-based bulk metallic glasses show high glass forming ability and are attractive base materials for near future additive applications. A new composition was printed by in-situ alloying from elemental powders via selective laser melting. In order to obtain a glassy, crack-free and dense bulk parts, a wide range of laser and scanning parameters were used and optimized. An SLM machine equipped with CO2 laser resulted in different amounts of un-melted Zr powder residues at both low and high energy density levels. Microscopic results indicate a positive trend with respect to the fraction of un-melted Zr powder for higher energy densities. However, the production of thoroughly melted and homogenized parts remains an open challenge. Segregation of Zr powder and its chemical deviation inhibited the formation of a fully glassy structure, although the cooling rates achieved during processing were much higher than the ones required to obtain fully amorphous structures. The result of this parameter study confirms that with respect to the formation of a glassy structure several challenges have to be addressed. The process optimization has to involve customization of every single parameter e.g. in terms of raw powder specification, spot size (energy distribution) and substrate material for each new composition.
One of the key restrictions of conventional technologies is that you have to choose between large quantities of same design with low costs or small quantities of individualized design with high costs. Additive Manufacturing (AM) enables us now to overcome this restriction. It is now possible to print different designs in the same process. This leads to the possibility to reduce the production costs of individualized parts close to the level of standardized AM parts. To forward this benefit to the customer it is necessary to develop a flexible design solution that is easy to modify by the customers input. These developments we want to show at our newly developed flowfilters. We developed those to optimize the injection molding process. With the design advantages of AM we could reduce the pressure drop to an unprecedented minimum while increasing the filter performance. Furthermore, optional mixing is possible to improve the material homogeneity of the injected plastic. This part offers even with standard design huge customer benefits with competitive costs. As currently many customer have additionally the need to individualized solutions, which were not available on the market with a reasonable pricing, yet. Based on a highly parametrized design we can now offer our customers a high degree of individualization with a competitive pricing. In this case, we can clearly show the huge potential of AM to improve long-term established and well-optimized parts and create a huge customer benefit.
The speech will also focus on the production of Metal Powders and Powder Metallurgical Steels and especially its associated production technologies like HIP, MIM and AM. As they are and will become key future core technologies for a number of demanding products and thus for the usage in different associated industries. The presentation will also highlight the actual supply and demand situation of metal powders and the manufactured metal powder steels, will introduce leading manufacturers of both powders and steels, and summarizes installed capacity and new capacity that are on the way as well as new players that enter this high value industry. The presentation will also highlight the recent developments in the world of Forged Special Steels and remelted steels (nickel alloys, stainless steel, alloy tool steel and alloy steel) as well as will give an overview about end-user demand and structures of these special steels and also summarize the actual status of installations on a global scale.
To accurately describe the Selective Laser Melting with the goal to study residual stress development and deformations induced by the manufacturing process is very challenging due to the complex physics of the process. A concentrated, fast moving heat source on a very small scale in intricate patterns, multiphysics and metallurgy combined creates quite a challenge. In this work, methods from the field of Verification and Validation are applied to quantify the predictive capacity of the employed simulation tools.
In the project, a Design of Experiments approach was utilized whereby several input variables (specimen geometry and manufacturing process parameters) were varied. For each of the DoE points a physical specimen was manufactured which was then subjected to a cutting operation resulting in a geometrical distortion due to the residual stress state. The change in geometry was measured both using Digital Image Correlation (DIC) and laser scanning. The obtained data was then used to evaluate the predictive capacity of the employed simulation tools.
Macroscopic input variables like cantilever thickness and preheater temperature are evaluated with macroscopic simulation methods (low-resolution simulation) while microscopic input variables like scan geometry are evaluated with microscopic (high resolution) methods. The low-resolution simulation methods are Simufact mechanical (inherent strain) and thermomechanical solvers on a component scale. The high resolution simulations are FCC:s in-house LastFEM on up to 10 power layer scale. The high-resolution simulation has also been evaluated to provide inherent strain distribution input to low resolution mechanical simulation. Extensive material characteristics for maraging tool steel grade has been provided from Uddeholm.
The project illustrates how validation approaches can be used to support the process of developing and evaluating simulation tools and their ability to predict the characteristics of a component manufactured through additive manufacturing.
The Danish industry has been reluctant to adopt Metal AM, despite the enormous potential for tailored and flexible manufacturing. A national granted project called: “AM-LINE 4.0” (2018 – 2021) has paved the way for the Danish manufacturing industry by removing barriers preventing implementation. The project has a total budget of 12M EUR and is a partnership with the leading industrial partners: Grundfos, Danfoss, SLM Solution, and TWI; together with The Danish Technical University.
The Danish Technological Institute is project manager, and this oral presentation will summarize the main results of the project from a combined industrial and academic point of view. The following topics will be discussed during the presentation:
• Identification of business cases in large organizations and redesign for Metal AM. Examples for Grundfos and Danfoss will be shown together with State-of-the-Art optimization methods as: Distortion compensation with thermomechanical simulations, lattice structures, and thermal topology optimization.
• Quality Assurance procedures for Metal AM by utilizing IoT. An effective cloud-based storing of all production data, that can be used to make cost-effective Quality Control - combined with the main results from the article: “Towards a digital twin of laser powder bed fusion with focus on gas flow variables” [Klingaa, et al] will be submitted later in February 2021 to Elsevier Journal of Manufacturing Process.
• Various micro- and macro-based modelling approaches on laser powder bed will be discussed. These models cover different topics as for instance: Micromechanics and fatigue life estimation, tailored heat treatments of additively manufactured materials, porosity estimation, and geometrical distortion. Several publications have been made by the Danish Technical University and this presentation will cover an overview of the main results.
Additive manufacturing makes it possible to produce highly complex components such as turbine blades with integrated cooling channels directly from a digital 3D CAD model. However, the material selection of nickel-base superalloys for the laser powder bed fusion (LPBF) process is limited to a few alloys that reveal a high printability, such as IN625 or IN718. These alloys, however, exhibit only moderate high-temperature and creep properties compared to nickel-base superalloys with higher γ′-content, such as CM247LC, that currently cannot be produced crack-free via LPBF.
Based on an industrially widely used but not yet printable reference alloy CM247LC, adjustments to the chemical composition (e.g., C, Hf, Ti, Al content) are made to improve processability with LPBF. High-throughput CALPHAD-based screening is applied to pre-select promising chemical compositions from a multidimensional alloy space with respect to specific target properties to accelerate alloy development significantly. In the following, the melt pool geometries, 3D temperature distributions, cooling rates, and thermal gradients during the LPBF process of selected alloy compositions are simulated with CFD-melt pool simulations. The melt pool simulation results are essential to simulate the solidification behavior and microstructure development of adapted AM nickel-base superalloys with high γ′-content by a phase-field approach in the following. Based on the computational alloy design approach, strategies for improving the processability of high γ′ nickel-base superalloys are discussed.
Additive manufacturing (AM) of cold work tool steel is challenging due to the material’s proneness to thermal cracks and defects. These issues can be reduced by the use of electron powder bed fusion (E-PBF) manufacturing which provides higher build chamber temperature, pre-heating of the build and slower cooling of the builds compared to laser powder bed fusion (L-PBF). Still, microstructure and properties of the as-build parts significantly differ from the conventional manucaftured material, so post treatment is required to achieve high levels of required characteristics. This research reveals the influence of heat treatment and heat treatment + HIP on defects, microstructure and properties of E-PBF high-alloy (Cr-Mo-V) tool steel. Focus is paid on changes in carbide type and morphology, analysis of prior austenite grain size, elimination of defects and morphology of martensite. A correlation between changes in microstructure and mechanical properties of heat-treated and HIPed E-PBF high-alloy (Cr-Mo-V) tool steel is discussed in a comparison to microstructure and properties of conventionally manufactured materials.
Critical components made of high-performance materials subjected to fatigue
loads have extreme demands on qualification and production control. Additive
Manufacturing is now an increasingly important technology for implementation
of bionic lightweight designs.
Over recent years, a great deal of research work has been carried out on additively manufactured
grade 5/23 titanium (Ti6Al4V) in safety-critical applications such as aerospace, medical or car racing.
Lightweight designs bring about lower safety margins, which in turn create a need for high fatigue
strength together with a robust production process resulting in a very low standard deviation of
mechanical material properties.
Post-processing, mainly consisting of hot-isostatic pressing (HIP), heat treatment (HT) and surface
finishing, is an integral part of a robust production process and should be ideally tailored to a
particular alloy. This is especially interesting and rewarding in the case of such a widely-used and
well-researched alloy as Ti6Al4V, taking the best out of both the novel microstructure of the AM
process as well as of more established heat treatment methods known from forgings or castings.
High-pressure Heat Treatment (HPHT), developed by Quintus Technologies for combining traditional
HIP cycles with an integrated, subsequent inert gas quenching cycle is used with great advantage on
additively manufactured Ti6Al4V for maximizing the fatigue strength in a lean, fast and robust process.
The microstructure of laser powder bed fusion (L-PBF) processed 18Ni300 differs from that of manufactured using conventional processing routes. The L-PBF steel, due to the non-equilibrium solidification, comprises a cellular/dendritic solidification structure with the presence of intercellular austenite as a result of heavy micro-segregation of alloying elements. On the other hand, the conventionally manufactured counterpart shows a fully martensitic microstructure in solution annealed condition. This difference appears to be insignificant in view of the static mechanical properties (e.g., tensile properties) after ageing heat treatment. Therefore, it is suggested that the L-PBF 18Ni300 can be directly aged from the as-built condition without a need for prior microstructural homogenization. However, the influence of the initial microstructure on the dynamic mechanical properties of the age hardened parts such as impact toughness, and fatigue resistance has not been systematically studied. In this work, the effect of homogenization and solution annealing treatment prior to ageing on mechanical properties and fatigue resistance of an 18Ni300 maraging steel is investigated. The results show an improvement of fatigue resistance by application of proper homogenization heat treatments.
Additive Manufacturing (AM) technologies provide new opportunities to enhance some piece-producing processes in the industry: AM offers the possibility to produce complex-shaped parts that could require multiple manufacturing stages. Moreover, microstructures from Laser Powder Bed Fusion (LPBF) can heavily differ from microstructures usually obtained through traditional processes, showing extremely fine cells caused by the rapid cooling.
In this work, several LPBF preforms were constructed along different directions in order to study the anisotropic properties inherited by the LPBF technology. Then, the as-built samples were cold rolled at different deformation rates. Two 316L powders that produce two different microstructures were used: one exhibiting columnar grains and the other quasi-equiaxed ones. Optical microscopy (OM) and scanning electron microscopy along with electron backscatter analyses (SEM-EBSD) were used to determine the microstructural evolutions. Tensile testing was carried out to determine the mechanical properties.
The first results show that the LPBF 316L is ductile while being more resistant than the traditional wrought 316L. In addition, the orientation of the building direction (BD) compared to the rolling direction (RD) seems to have an influence on the material properties during cold rolling. Indeed, mechanical twins were observed when the BD is collinear to the RD while slip bands are present when the BD is orthogonal to the RD, even if one of the studied microstructure is almost isotropic with quasi-equiaxed grains and almost no texture.
The final goal of this study is to analyse the potentialities of integrating the LPBF technology in the conventional manufacturing processes. This integration would then simplify and enhance key parts production, especially in the nuclear industry.
Maraging steels are a class of ultra-high-strength martensitic steels, strengthened by precipitation of intermetallic particles in the Fe-Ni martensite upon aging. Due to their low carbon content, these steels demonstrate excellent weldability and negligible dimensional changes after heat treatment, and hence several types of maraging steels have been developed for laser-based additive manufacturing (AM) during the past decade. AM-MAR60HRC is a recently developed powder for AM to satisfy the requirements in some demanding applications, reaching strength levels up to 2600 MPa (~60HRC). This steel can be hardened in several minutes in the temperature ranges of 450-600°C, making it a proper candidate for Direct Laser Metal Deposition (DLMD), specifically for tooling applications, as it is suitable for very localized heat treatments on the deposited surface without affecting the core material hardness and strength. This work aims to investigate the processing parameters, and to study the microstructure and aging behavior of DLMD-MAR60HRC.